| Keperluan Tegangan dan Kekerasan |
| Gred |
|
|
Kekuatan Hasil MPa |
Tegangan Kekuatan |
Kekerasan a,c |
Ketebalan Dinding Yang Ditentukan |
Kekerasan Yang Dibenarkan Variasi b |
| |
Jenis |
Jumlah Pemanjangan Di Bawah Beban |
|
min MPa |
maks |
|
|
| |
|
|
min |
maks |
|
HRC |
HBW |
mm |
HRC |
| 1 |
2 |
3 |
4 |
5 |
6 |
7 |
8 |
9 |
10 |
| H40 |
|
0.5 |
276 |
552 |
414 |
|
|
|
|
| J55 |
|
0.5 |
379 |
552 |
517 |
|
|
|
|
| K55 |
|
0.5 |
379 |
552 |
655 |
|
|
|
|
| N80 |
1 |
0.5 |
552 |
758 |
689 |
|
|
|
|
| N80 |
Q |
0.5 |
552 |
758 |
689 |
|
|
|
|
| R95 |
|
0.5 |
655 |
758 |
724 |
|
|
|
|
| l80 L80 |
1 |
0.5 |
552 |
655 |
655 |
23 |
241 |
|
|
| L80 |
9Cr 13Cr |
0.5 |
552 |
655 |
655 |
23 |
241 |
|
|
| |
|
0.5 |
552 |
655 |
655 |
23 |
241 |
|
|
| C90 |
1 |
0.5 |
621 |
724 |
689 |
25.4 |
255 |
12.70 |
3 |
| |
|
|
|
|
|
|
|
12.71 hingga 19.04 |
4 |
| |
|
|
|
|
|
|
|
19.05 hingga 25.39 |
5 |
| |
|
|
|
|
|
|
|
25.40 |
6 |
| T95 |
1 |
0.5 |
655 |
758 |
724 |
25.4 |
255 |
12.70 |
3 |
| |
|
|
|
|
|
|
|
12.71 hingga 19.04 |
4 |
| |
|
|
|
|
|
|
|
19.05 hingga 25.39 |
5 |
| |
|
|
|
|
|
|
|
25.40 |
6 |
| C110 |
|
0.7 |
758 |
828 |
793 |
30 |
286 |
12.70 |
3 |
| |
|
|
|
|
|
|
|
12.71 hingga 19.04 |
4 |
| |
|
|
|
|
|
|
|
19.05 hingga 25.39 |
5 |
| |
|
|
|
|
|
|
|
25.40 |
6 |
| P110 |
|
0.6 |
758 |
965 |
862 |
|
|
|
|
| Q125 |
1 |
0.65 |
862 |
1034 |
931 |
b |
|
12.70 |
3 |
| |
|
|
|
|
|
|
|
12.71 hingga 19.04 19.05 |
4 |
| |
|
|
|
|
|
|
|
|
5 |
| a Sekiranya berlaku pertikaian, ujian kekerasan makmal Rockwell C hendaklah digunakan sebagai kaedah pengadil. |
| b Tiada had kekerasan dinyatakan, tet API variasi maksimum dihadkan sebagai kawalan pembuatan mengikut 7.8 dan 7.9. |
| c Untuk ujian kekerasan melalui dinding Gred L80 (semua jenis), C90, T95 dan C110, keperluan yang dinyatakan dalam skala HRC adalah untuk nombor purata kekerasan maksimum. |